Refractory castables mainly include common series,low-cement series, ultralow cement series and lightweight series,Which are used respectively for the following aspects according to their various features :
a. For hot blast stove system,secondary refining devices,up-take pipe lining,pretreatment hot metal ,lance for oxygen and argon blowing;
b. For steel making and steel rolling systems,EAF roof,triangle area of EAF roof,ladle,reheating furnace,soaking pit,inner lining of heat treating furnace,pre-cast block for water-cooling slide rails,soot blowing port，burner and fire blocking port.
c. For cement kiln,lining of tube Cooler,roof and innerlining on the cell bottom of float glass tank ,
petroleum cracking reactor,high-ternperature and abrasion resistant lining,Synthetic ammonia device and lining for gas furnace.
|
Item |
Index |
|||
|
WMJ-1 |
WMJ-2 |
WMJ-3 |
||
|
Al2O3,% |
≥60 |
≥65 |
≥70 |
|
|
BD.g/cm3 |
110℃×24h After drying |
≥2.40 |
≥2.60 |
≥2.80 |
|
CCS,MPa |
110℃×24h After drying |
≥55 |
≥60 |
≥65 |
|
1000℃×3h After sintering |
≥80 |
≥90 |
≥100 |
|
|
CMOR,MPa |
110℃×24h After drying |
≥7 |
28 |
≥9 |
|
1000℃×3h After sintering |
≥9 |
≥11 |
≥13 |
|
|
PLC,% |
1000℃×3h |
±0.3 |
±0.3 |
±0.3 |
|
Amount of wear at room temp,cm3 |
1000℃×3h After sintering |
≤9 |
8 |
7 |
|
TSR,Cyele |
1000℃, Water cooling |
≥20 |
≥20 |
≥20 |
|
Max.service temperature,℃ |
1400 |
1450 |
1500 |
|
Key words:
Refractory Castables
Previous page:
Next page:
Related Products
Leave a message
Leave your contact information and we will contact you during business hours
Tel:
Email:
Email: FuHao Office in Pakistan
Contact